PU drying temperature depends on hardness. 60A-80A drying temperature is 90-100 degrees 85A-98A drying temperature is 100-105 degrees 60D-71D drying temperature and 105-110 degrees drying time is 3-5 hours.
LCP
Each company has different drying temperature and forming temperature for different varieties. For example, the best forming temperature of EI series of Japanese Poly Company is 340-370, and the upper limit of 365 degrees is not more than 30 minutes.
PA Properties
Crystalline thermoplastics have obvious melting point, Nylon 6 Tm is 220-230 C, Nylon 66 is 260-270 C. Nylon itself has water absorption base, so it must be dry before forming. If the temperature is too high and dry, nylon particles will change color.
PC/ABS
The specific gravity is generally 1.15, the water absorption is 0.2%, the shrinkage is 0.4-0.6, and the hot deformation temperature is 120%. The drying temperature should be 100, and the drying temperature should be 100-110 degrees for 3-4 hours.
AS
The injection pressure of nozzle 190-210 degree should be 50-60 degree, the holding pressure should be 40-50 degree, the mould temperature should be 50-70 degree, the screw speed should be 40-60 degree, the back pressure should be 5-10 degree, the drying temperature should be 80-100 degree, and the drying time should be 2-4H.
PBT
Nozzle temperature 230-245 injection pressure 70-120, holding pressure 40-50, mould temperature 50-160, screw speed 40-70, back pressure 5-10, drying temperature 100-140, drying time 4-6 hours.
PET
Nozzle 240-270, injection pressure 70-100, holding pressure 40-50, mould temperature 50-160, screw speed 40-75, screw back pressure 5-10, baking temperature 100-140, baking time 6-8 hours.
PC
Nozzle 270-300, mould temperature 80-120, drying temperature 100-120, drying time 2-4 hours.
PA6
Nozzle 250-260, mould temperature 50-110, drying temperature 80-110, drying time 4-6 hours.
PA66
Nozzle 250-280, mould temperature 50-110, drying temperature 80-130, drying time 4-6 hours.
PPS
Nozzle 290-300, mould temperature 80-150, baking temperature 120-140, baking time 2-4 hours.
LCP
Nozzle 300-310, mould temperature 90-180, baking temperature 130-140, baking time 2-4 hours.
POM
Nozzle 170-230, mould temperature 50-80, baking temperature 80-120, baking time 2-4 hours.
PP
Nozzle 200-220, mould temperature 40-60, baking temperature 80-120, baking time 2-4 hours.
PPO
Nozzle 210-260, mould temperature 50-90, baking temperature 80-140, baking time 2-4 hours.
PEI
Nozzle 300-320, mould temperature 180-200, baking temperature 120-140, baking time 2-4 hours.
PEEK
Nozzle 310-360, mould temperature 120-160, baking temperature 120-140, baking time 2-4 hours.
PA46
Nozzle 290-300, mould temperature 80-120, baking temperature 290-300, baking time 2-4 hours.